Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 18.0 cm3/10min |
| spiral flow length | | 内部方法 | 29.0 CM |
| Shrinkage rate | | 内部方法 | 0.50 - 0.70 % |
| Shrinkage rate | | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | | ISO 62 | 0.23 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 50 |
| Rockwell hardness | | ISO 2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| ISO 9660 | | | >PC< |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 65.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 95 % |
| Flexural modulus | | ISO 178 | 2300 Mpa |
| bending strength | | ISO 178 | 90.0 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| dielectric constant | | IEC 60250 | 2.85 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 5.0 to 8.0 hr |
| Temperature at the rear of the barrel | | | 260 to 300 °C |
| Temperature in the middle of the barrel | | | 260 to 300 °C |
| Temperature at the front of the material cylinder | | | 260 to 300 °C |
| Temperature | | | 80 to 120 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 125 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 80.0 °C |
| RTI Imp | | UL 746 | 80.0 °C |
| RTI | | UL 746 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.