PC LNP™ LUBRICOMP™ DFL32XXP compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.67 % | |
| ASTM D955 | 0.20 % | ||
| density | ASTM D792 | 1.37 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.23 % | |
| ASTM D955 | 0.70 % | ||
| Water absorption rate | ASTM D570 | 0.11 % | |
| ISO 62 | 0.18 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Break | ISO 527-2 | 71.0 MPa |
| Flexural modulus | ISO 178 | 4170 MPa | |
| ASTM D790 | 4350 MPa | ||
| bending strength | ASTM D790 | 124 MPa | |
| Tensile strain | Break | ISO 527-2 | 2.8 % |
| elongation | Break | ASTM D638 | 3.1 % |
| tensile strength | Break | ASTM D638 | 73.4 MPa |
| Tensile modulus | ASTM D638 | 4350 MPa | |
| ISO 527-2/1 | 4290 MPa | ||
| bending strength | ISO 178 | 114 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 11.6 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.29 J | |
| Impact strength of cantilever beam gap | ASTM D4812 | 530 J/m | |
| ISO 180/1A | 10 kJ/m² | ||
| ASTM D256 | 91 J/m | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 34 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 141 °C | |
| ISO 75-2/Af | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.