Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO11443-A | 410 Pa·s |
| density | | ISO1183 | 1.19 g/cm³ |
| Melt volume flow rate | | ISO1133 | 11.0 cm³/10min |
| Shrinkage rate | | ISO2577 | 0.50to0.70 % |
| Shrinkage rate | | ISO2577 | 0.50to0.70 % |
| Water absorption rate | | ISO62 | 0.50 % |
| Water absorption rate | | ISO62 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | 5VB |
| UL flame retardant rating | | UL94 | 5VA |
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/50 | 69.0 MPa |
| Tensile stress | | ISO527-2/50 | 53.0 MPa |
| Tensile strain | | ISO527-2/50 | 5.0 % |
| Tensile strain | | ISO527-2/50 | >50 % |
| Tensile modulus | | ISO527-2/1 | 2650 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 40 kJ/m² |
| | ISO180 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC60243-1 | 35 kV/mm |
| Surface Resistivity | | IEC60093 | 1E+17 ohms |
| | IEC60250 | 3.20 |
| | IEC60250 | 3.10 |
| Dissipation Factor | | IEC60250 | 3.7E-03 |
| Dissipation Factor | | IEC60250 | 7.5E-03 |
| CTI | | IEC60112 | 350 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 106 °C |
| | ISO75-2/A | 98.0 °C |
| vicat | | ISO306/B50 | 113 °C |
| vicat | | ISO306/B120 | 115 °C |
| | ISO11359-2 | 6.8E-05 cm/cm/°C |
| | ISO11359-2 | 7.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.