ABS HM42
0
- Properties:High heat resistancemedium impact resistance
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.04 g/cm3 | |
| Shrinkage rate | ASTM D955 | 0.60-0.80 % | |
| density | ASTM D792 | 1.04 g/cm³ | |
| Shrinkage rate | ASTM D995 | 0.60-0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 100 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 100 R 计秤 | |
| elongation at yield | ASTM D638 | 42.7 % | |
| Flexural modulus | ASTM D790 | 2210 MPa | |
| bending strength | ASTM D790 | 68.9 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 220 J/m | |
| bending strength | ASTM D790 | 68.90 MPa | |
| Flexural modulus | ASTM D790 | 2210 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 220 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 3.18mm | |
| UL -94 | HB 1.59mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 97.8 ℃ | |
| UL flame retardant rating | UL 94 | HB | |
| Heat distortion temperature | ASTM D648 | 97.80 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.