Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate for 24 hours in water | | ASTM D570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness R scale | | ASTM D785 | 119 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM DI 003 | 90.2 % |
| Haze ratio | | ASTM D1003 | 1.1 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength yield 50mmzmin | | ASTM D638 | 51 Mpa |
| Tensile strength fracture 50mm/min | | ASTM D638 | 29.2 Mpa |
| Elongation yield 50mm/min | | ASTM D638 | 5.1 % |
| Elongation fracture 50mm/min | | ASTM D638 | 88 % |
| Bending leakage rate of 1.27mm/min | | ASTM D790 | 70.8 Mpa |
| Bending modulus 1.27mm/min | | ASTM D790 | 2090 Mpa |
| | ASTM D256 | 51 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D257 | 1230000000000000 Ω.cm |
| Surface Resistivity | | ASTM D257 | 10500000000000000 Ω |
| Absolute source intensity 2kV/s short-term | | ASTM D149 | 15.83 KV/mm |
| dielectric constant | | ASTM DI50 | 2.32 |
| dielectric constant | | ASTM D150 | 2.13 |
| Dissipation Factor | | ASTM DI 50 | 0.0058 |
| Dissipation Factor | | ASTM DI 50 | 0.0246 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature 0.45MPa | | ASTM D648 | 76.2 °C |
| Hot deformation temperature 1.8MPa | | ASTM D648 | 66.2 °C |
| Vicat softening temperature 10N | | ASTM D1525 | 79.1 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.