Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619-1 | 76 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ISO 13468 | 92.0 % |
| transmissivity | | CSA LISTED | 64 to 66 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | -- Mpa |
| tensile strength | | ISO 527-2 | -- Mpa |
| Tensile strain | | ISO 527-2 | -- % |
| Nominal tensile fracture strain | | ISO 527-2 | > 50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| drying time | | | 4.0 to 6.0 hr |
| Processing (melt) temperature | | | 260 to 300 °C |
| Temperature | | | 20 to 80 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 85.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 73.0 °C |
| Glass Transition Temperature | | ISO 11357-2 | 101 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices