PBT HCG2520MP JAPAN POLYPLASTIC

Form：Granules

Properties:

Glass fiber reinforcedFlame retardant

Typical Applications:

Home appliance componentsElectronic and electrical components

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Electronic and electrical components
Properties:	Glass fiber reinforced \| Flame retardant

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	100	Mpa
elongation	Break	ASTM D638	2.0	%
Bending modulus		ASTM D790	5700	Mpa
bending strength		ASTM D790	172	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100 to 120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Temperature at the rear of the barrel			250 to 270	°C
Temperature in the middle of the barrel			260 to 280	°C
Temperature at the front of the material cylinder			280 to 300	°C
Spray nozzle temperature			280 to 290	°C
Processing (melt) temperature			290 to 300	°C
Mold temperature			100 to 140	°C
Back pressure			0.300 to 1.00	Mpa
Screw speed			20 to 100	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	137	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Shrinkage rate	Flow	ASTM D955	0.10 - 0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.