PA6 SOLLAMID B 2700 MW Krisoll Resinas Plásticas Ltda.

Compare

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break	23°C	ASTM D638	3 %
Tensile modulus	23°C	ASTM D638	6700 MPa
bending strength	23°C	ASTM D790	150 MPa
Bending modulus	23°C	ASTM D790	5800 MPa
Impact strength of cantilever beam gap	23°C	ASTM D256	55 J/m
tensile strength	23°C	ASTM D638	90 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPaUnannealed	ASTM D648	185 °C
Hot deformation temperature	Hot deformation temperature	1.80MPaUnannealed	ASTM D648	140 °C
Vicat softening temperature	Melting Temperature		214-220 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.46 g/cm³
Shrinkage rate	MD	ASTM D995	0.80-1.0 %
Water absorption rate	(23°C,24hr)	ASTM D570	0.90-1.0 %
Water absorption rate	Water absorption rate	热稳定性		90-100 ℃

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1E+12 Ω.cm
Dielectric strength		ASTM D149	15 KV/mm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	120 R

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	V-2 1.60mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.