Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.33 g/cm³ |
| Water absorption rate | | ISO 1110 | 1.8 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO 1172 | 30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | >100 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 20 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 25 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | >100 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Fracture bending strain | | ISO 178 | 5.0 % |
| Tensile modulus | | ISO 527-2/1 | 9000 MPa |
| tensile strength | Break | ISO 527-2/5 | 160 MPa |
| Tensile strain | Break | ISO 527-2/5 | 5.0 % |
| Flexural modulus | | ISO 178 | 8500 MPa |
| bending strength | | ISO 178 | 265 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 220 °C |
| Heat distortion temperature | | ISO 75-2/A | 205 °C |
| melting temperature | | DIN EN11357-1 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.