PP AP03B EXXONMOBIL SINGAPORE

103

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh mobilityEasy to processHigh crystallinityHigh rigidityFast forming cycle

Typical Applications:

Industrial applicationsHome appliance componentsAutomotive sectorAutomotive interior partsConsumer goods sectorApplication in the automotive fieldConsumer product application field

Supplier(1)

Product Description

Certificates(3)

Datasheet

Alternative Model(1)

Product Description

Typical Applications:	Industrial applications \| Home appliance components \| Automotive sector \| Automotive interior parts \| Consumer goods sector \| Application in the automotive field \| Consumer product application field
Properties:	High impact resistance \| High mobility \| Easy to process \| High crystallinity \| High rigidity \| Fast forming cycle

Certificates

TDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.4	kJ/m²
	Charpy Notched Impact Strength	-20°C	ISO 179/1eA	3.8	kJ/m²
		Charpy Notched Impact Strength	0°C	ISO 179/1eA	4.2	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.6	kJ/m²
Impact strength of cantilever beam gap	-18°C	ASTM D256A	34	J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256A	72	J/m
		Impact strength of cantilever beam gap	-40°C	ISO 180/1A	2.9	kJ/m²
			Impact strength of cantilever beam gap	-18°C	ISO 180/1A	4.1	kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.9	kJ/m²
Dart impact	-29°C,3.18mm	ASTM D5420	17.3	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	1440	Mpa
tensile strength	Yield3	ASTM D638	26.6	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	25.1	Mpa
elongation	Yield3	ASTM D638	5.0	%
elongation	elongation	Yield	ISO 527-2/50	4.9	%
Bending modulus	1%Secant4	ASTM D790A	1310	Mpa
	Bending modulus	1%Secant5	ASTM D790B	1500	Mpa
	Bending modulus	Bending modulus	--6	ISO 178	1260	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Annealed	ASTM D648	119	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	54.6	°C
		Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	105	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	93.5	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	30	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.