Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.17 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 15到45 g/10min |
| Shrinkage rate | | ASTMD955 | 1.3 % |
| Shrinkage rate | | ASTMD955 | 1.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 89到91 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Dynamic Properties | | | 0.0440 |
| Dynamic Properties | | | 0.0530 |
| Dynamic Properties | | | 1.33E+08 dynes/cm² |
| Dynamic Properties | | | 6.3E+07 dynes/cm² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTMD790 | 28.5 MPa |
| Wear resistance - DIN | | DIN53516 | 16.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ASTMD412 | 7.52 MPa |
| tensile strength | | ASTMD412 | 30.8 MPa |
| elongation | Break | ASTMD412 | 570 % |
| tear strength | | ASTMD470 | 28 kN/m |
| tear strength | Split | ASTMD470 | 30 kN/m |
| compression set | | ASTMD395B | 28 % |
| Basho elasticity | | ASTMD2632 | 55 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Tear resistance of pants | | ASTMD1938 | 78.3 N/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | -34.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.