Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792A | 1.35 g/cm³ |
| Water absorption rate | | 内部方法 | 0.15 % |
| Decomposition Temperature | | 内部方法 | 368 °C |
| Decomposition Temperature | | 内部方法 | 354 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| T | | 内部方法 | >1.0 hr |
| T | | 内部方法 | >30.0 min |
| T | | 内部方法 | 15.0 min |
| ExpansionRate | | 内部方法 | 2.6 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | 内部方法 | 17900 MPa |
| tensile strength | | 内部方法 | 44.8 MPa |
| bending strength | | 内部方法 | 579 MPa |
| film | Test Condition | Test Method | Test Result |
|---|
| peelstrength | | 内部方法 | 1.6 kN/m |
| peelstrength | | 内部方法 | 1.2 kN/m |
| peelstrength | | 内部方法 | 1.1 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | 内部方法 | 2.9E+13 ohms |
| Surface Resistivity | | 内部方法 | 4E+12 ohms |
| Volume resistivity | | 内部方法 | 2.6E+13 ohms·cm |
| Volume resistivity | | 内部方法 | 3.3E+06 ohms·cm |
| dielectric strength | | 内部方法 | 39 kV/mm |
| dielectric constant | | 内部方法 | 4.20 |
| dielectric constant | | 内部方法 | 4.10 |
| Dissipation Factor | | 内部方法 | 0.020 |
| Dissipation Factor | | 内部方法 | 0.020 |
| arc resistance | | 内部方法 | >120 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | 内部方法 | 2.5E-04 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.25 W/m/K |
| Glass Transition Temperature | | 内部方法 | 166 °C |
| Glass Transition Temperature | | 内部方法 | 170 °C |
| | 内部方法 | 1.3E-5到1.5E-5 cm/cm/°C |
| | 内部方法 | 4.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare