POM UV140LG-BK CELANESE USA

Form：Granules | Grade：Injection grade

Properties:

Low glossHigh mobility

Typical Applications:

Automotive sectorAutomotive interior parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Automotive interior parts
Properties:	Low gloss \| High mobility

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A	2100	Mpa
tensile strength	Yield	ISO 527-2/1A/50	48.0	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	10	%
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100 to 120	°C
drying time			3.0 to 4.0	hr
Temperature at the rear of the barrel			170 to 175	°C
Temperature in the middle of the barrel			170 to 180	°C
Temperature at the front of the material cylinder			175 to 185	°C
Spray nozzle temperature			185 to 195	°C
Processing (melt) temperature			180 to 195	°C
Mold temperature			80 to 105	°C
Injection speed			慢
Back pressure			< 4.00	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	85.0	°C
Melting temperature		ISO 11357-3	168	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	190°C/2.16 kg	ISO 1133	13.0	cm3/10min
Shrinkage rate	横向Flow	ISO 294-4	1.8	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	2.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.