PC L-1250Z TEIJIN SINGAPORE

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanLow temperature resistancheat-resistingtransparent

Typical Applications:

Nursing suppliesDisposable tablewareMedical suppliesElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Nursing supplies \| Disposable tableware \| Medical supplies \| Electronic field \| Electrical field
Properties:	High temperature resistan \| Low temperature resistanc \| heat-resisting \| transparent

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.585
transmissivity	3000 μm	ASTM D1003	88.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	无断裂
Charpy Notched Impact Strength		ISO 179	76	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.40 mm	UL 94	V-2
Burning wire flammability index	1.5 mm	IEC 60695-2-12	825	°C
Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	875	°C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	93.0	Mpa
Bending modulus		ISO 178	2350	Mpa
Nominal tensile fracture strain		ISO 527-2/50	> 50	%
Tensile strain	Yield	ISO 527-2/50	6.0	%
tensile strength	Yield	ISO 527-2/50	61.0	Mpa
Tensile modulus		ISO 527-2/1	2400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI	0.75 mm	UL 746	125	°C
RTI Imp	0.75 mm	UL 746	115	°C
RTI Elec	0.75 mm	UL 746	125	°C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	7.0E-5	cm/cm/°C
Vicat softening temperature		ISO 306/B50	149	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	129	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	142	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.20	g/cm³
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	8.00	cm3/10min
Shrinkage rate	横向Flow : 4.00 mm	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	Flow : 4.00 mm	Internal Method	0.50 - 0.70	%
Water absorption rate	24 hr, 23°C	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 2
Dissipation factor	1 MHz	IEC 60250	9.0E-3
Dissipation factor	Dissipation factor	100 Hz	IEC 60250	1.0E-3
Relative permittivity	1 MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	100 Hz	IEC 60250	3.10
Dielectric strength		IEC 60243-1	30	KV/mm
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Surface resistivity		IEC 60093	> 1.0E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.