Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.12 g/cm³ |
| density | | ISO 1183 | 1.12 g/cm³ |
| Apparent viscosity | | ASTM D3835 | 170 Pa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 61 |
| Shore hardness | Shore A | ISO 868 | 61 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Taber abraser | | ASTM D1044 | 0.0310 mg |
| Taber abraser | | ASTM D1044 | 0.333 mg |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| compression set | | ISO 815 | 16 % |
| compression set | | ISO 815 | 52 % |
| compression set | | ISO 815 | 66 % |
| Stretch permanent deformation | | ASTM D412 | 9 % |
| tensile strength | | ASTM D412 | 2.55 MPa |
| tensile strength | | ISO 37 | 2.55 MPa |
| tensile strength | Yield | ASTM D412 | 8.27 MPa |
| tensile strength | Yield | ISO 37 | 8.27 MPa |
| elongation | Break | ASTM D412 | 380 % |
| elongation | Break | ISO 37 | 380 % |
| tear strength | | ASTM D624 | 24.5 kN/m |
| tear strength | | ISO 34-1 | 25 kN/m |
| compression set | | ASTM D395A | 16 % |
| compression set | | ASTM D395A | 52 % |
| compression set | | ASTM D395A | 66 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| volume change | | ASTM D471 | -28 % |
| volume change | | ASTM D471 | -19 % |
| volume change | | ASTM D471 | -43 % |
| volume change | | ISO 1817 | -28 % |
| volume change | | ISO 1817 | -43 % |
| volume change | | ISO 1817 | -19 % |
| Change rate of tensile strength in air | | ASTM D573 | 130 % |
| Change rate of tensile strength in air | | ASTM D573 | 110 % |
| Change rate of tensile strength in air | | ISO 188 | 130 % |
| Change rate of tensile strength in air | | ISO 188 | 110 % |
| elongation at break | | ASTM D573 | 96 % |
| Change rate of ultimate elongation in air | | ISO 188 | 96 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -41.0 °C |
| brittle temperature | | ISO 812 | -41.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.