Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|
| | | 注射成型 |
| purpose | | | 高速注射, 容器 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 33 g/10min |
| density | | ASTM D-1505 | 0.950 g/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Izod notch impact strength | | ASTM D256/ISO 179 | 2 kg·cm/cm(J/M)ft·lb/in |
| Flexural modulus | | ASTM D790/ISO 178 | 8500 kg/cm²(MPa)[Lb/in²] |
| Tensile strength at break | | ASTM D-638 | 70 kg/cm |
| Yield tensile strength | | ASTM D-638 | 230 kg/cm |
| elongation | | ASTM D-638 | 270 % |
| IZOD impact strength | | ASTM D-256 | 2 kg.cm/cm |
| bending strength | | ASTM D-747 | 8500 kg/cm |
| surface hardness | | ASTM D-2240 | 61 Shore D |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| ESCR | | ASTM D-1693 | 2 hr |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.95 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 45 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525/ISO R306 | 122 ℃（℉） |
| melting point | | ASTM D-2117 | 130 °C |
| vicat | | ASTM D-1525 | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.