| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.32 -- |
| Shrinkage rate | | % | 1.0到1.3 -- |
| Water absorption rate | | % | 1.0到1.2 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 100 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | MPa | 100 55.0 |
| Tensile modulus | | MPa | 4600 2200 |
| tensile strength | | MPa | 60.0 50.0 |
| elongation | Break | % | 7.0 30 |
| Flexural modulus | | MPa | 3000 1600 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 60 110 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+12 -- |
| dielectric strength | | kV/mm | 15 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 110 -- |
| Continuous use temperature | | °C | 90.0到100 -- |
| | °C | 155 -- |
| melting temperature | | °C | 212到214 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.