Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 165 °C |
| melting temperature | | ISO 3146 | 225 °C |
| Maximum operating temperature - overnight | | | 160 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | 23°C | ISO 1183 | 1.34 g/cm³ |
| water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.3 % |
| tensile modulus | 23°C | ISO 527-2/1 | 7500 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare