Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | <0.10 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| Shrinkage rate | | ISO2577 | 0.40到0.60 % |
| density | | ISO1183 | 1.93到1.98 g/cm³ |
| Apparent density | | ISO60 | 0.80到0.90 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 900 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 900 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >5.00 MPa |
| CompressionMoldingTemperature | | | 150到190 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.0到4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 12到14 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 15000到18000 MPa |
| Tensile stress | | ISO527-2 | 70.0到90.0 MPa |
| Flexural modulus | | ISO178 | 15000到20000 MPa |
| Bending stress | | ISO178 | 140到160 MPa |
| compression stress | | ISO604 | 200到250 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+13到1.0E+14 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 25到35 kV/mm |
| | IEC60250 | 5.007.00 |
| | IEC60250 | 4.006.00 |
| Dissipation Factor | | IEC60250 | 0.030到0.050 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | 160到180 °C |
| | ISO11359-2 | 1.5E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 250 °C |
| maximum service temperature | | IEC60216 | 180 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.