| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.21 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 9.0to16 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Outdoor applicability | | UL 746C | f1 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 70 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 89.6 MPa |
| elongation | | ASTM D638 | 7.0 % |
| tensile strength | | ASTM D638 | 62.1 MPa |
| tensile strength | | ASTM D638 | 55.2 MPa |
| elongation | | ASTM D638 | 90 % |
| Flexural modulus | | ASTM D790 | 2210 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 640 J/m |
| Dart impact | | ASTM D3029 | >36.2 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 23 kV/mm |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| Volume resistivity | | ASTM D257 | 1E+17 ohms·cm |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Imp | | UL 746 | 110 °C |
| RTI Str | | UL 746 | 125 °C |
| RTI Str | | UL 746 | 125 °C |
| Heat distortion temperature | | ASTM D648 | 129 °C |
| vicat | | ASTM D15252 | 149 °C |
| RTI Elec | | UL 746 | 125 °C |
| RTI Elec | | UL 746 | 125 °C |
| Heat distortion temperature | | ASTM D648 | 135 °C |
| RTI Imp | | UL 746 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.