PPA HTN51G35HSL DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

enhanceGlass fiber reinforcedFlame retardantHigh temperature resistanThermal stabilityFood contact compliance

Typical Applications:

Automotive interior partsElectrical appliancesFitness equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electrical appliances \| Fitness equipment
Properties:	enhance \| Glass fiber reinforced \| Flame retardant \| High temperature resistan \| Thermal stability \| Food contact compliance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	23	mm/min
UL flame retardant rating	0.9mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.9mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	24	%
FMVSS flammability		FMVSS302	B
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	12000	Mpa
tensile strength	Break	ISO 527-2	210	Mpa
Tensile strain	Break	ISO 527-2	2.4	%
Tensile creep modulus	1hr	ISO 899-1	--	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	--	Mpa
Bending modulus		ISO 178	10300	Mpa
bending strength		ISO 178	300	Mpa
Poisson's ratio		ISO 527	0.39
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	284	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Melting temperature		ISO 11357-3	300	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1.8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	5.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	5.5E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	4.5	%
Shrinkage rate	TD	ISO 294-4	0.60	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.20	%
SpecificHeatCapacity of Melt			1860	J/kg/°C
ThermalConductivityofMelt			0.25	W/m/K
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	36	KV/mm
Relative permittivity	100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.00
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	108
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	124
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Odor		VDA270	4.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.