Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|---|---|---|
Humidity | ISO 15512/B | <0.25 % | |
density | ISO 1183 | 1.12 g/cm³ | |
ISO 1183/A | 1.12 g/cm³ |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Flexural modulus | ISO 178 | 1800 MPa | |
bending strength | ISO 178 | 80.0 MPa | |
Charpy Notched Impact Strength | ISO 179/1eA | 16 kJ/m² | |
ISO 179/1eU | 无断裂 | ||
Tensile modulus | ISO 527-2 | 2300 MPa | |
tensile strength | Break | ISO 527-2 | 60.0 MPa |
Tensile strain | Yield | ISO 527-2 | 3.5 % |
Break | ISO 527-2 | >25 % | |
Flexural modulus | ISO 178 | 1800 MPa | |
bending strength | ISO 178 | 80.0 MPa | |
Tensile modulus | ISO 527-2/1 | 2300 MPa | |
tensile strength | Break | ISO 527-2/5 | 60.0 MPa |
Tensile strain | Yield | ISO 527-2/5 | 3.5 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Charpy Notched Impact Strength | ISO 179/1eA | 16 kJ/m² | |
Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Heat distortion temperature | ISO 75-2/A | 55.0 °C | |
vicat | ISO 306 | > 200 °C | |
Heat distortion temperature | ISO 75-2/A | 55.0 °C | |
vicat | ISO 306/B | >200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.