| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.80to2.00 g/cm³ |
| Apparent density | | ISO 60 | 0.70to0.85 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.40to0.60 % |
| Water absorption rate | | ISO 62 | <0.20 % |
| Shrinkage rate | | ISO 2577 | <0.050 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO 527-2 | 4000to6000 MPa |
| tensile strength | | ISO 527-2 | 40.0to60.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 8000to10000 MPa |
| bending strength | Compression Molded | ISO 178 | 70.0to100 MPa |
| compression stress | | ISO 604 | 150to200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 2.5to4.5 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 4.0to6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 15to20 kV/mm |
| relative permittivity | | IEC 60250 | 4.005.00 |
| relative permittivity | | IEC 60250 | 4.005.00 |
| Dissipation Factor | | IEC 60250 | 0.010to0.030 |
| Dissipation Factor | | IEC 60250 | 0.010to0.030 |
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | >200 °C |
| Heat distortion temperature | | ISO 75-2/C | 150to170 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.0E-5到6.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40to0.60 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.