PEN

PEN NOPLA® KE101 KOLON KOREA

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	Total	ASTM D1003	85.0 %
turbidity		ASTM D1003	1.5 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ASTM D638	60.0 MPa
bending strength	23°C	ASTM D790	92.0 MPa
Bending modulus	23°C	ISO 178	2900 MPa
Bending modulus	Bending modulus	23°C	ASTM D790	2850 MPa
Tensile strain	Break,23°C	ISO 527-2	300 %
elongation	Break,23°C	ASTM D638	460 %
tensile strength	Yield,23°C	ISO 527-2	60.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ASTM D696	6E-05 cm/cm/°C
Melting temperature		ASTM D1525	234 °C
Melting temperature	Melting temperature		ISO 11357-3	230 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648A	77.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	75.0 °C

Physical properties	Test Condition	Test Method	Test Result
Intrinsic viscosity		Internal Method	0.88 dl/g
Water absorption rate	Equilibrium,23°C,60%RH	ASTM D570	0.070 %
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.10 %
Shrinkage rate		ISO 294-4	0.60 %
Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.40to0.60 %
melt mass-flow rate	275°C/2.16kg	ISO 1133	15 g/10min
melt mass-flow rate	melt mass-flow rate	260°C/1.05kg	ASTM D1238	8.1 g/10min
density		ISO 1183	1.33 g/cm³
density	density		ASTM D792	1.33 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	88
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	88

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.