PA9T GW2458HF-1BK KURARAY JAPAN

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedLow warpageHigh mobility

Typical Applications:

Electrical fieldElectronic fieldLaptop case

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Laptop case
Properties:	Glass fiber reinforced \| Low warpage \| High mobility

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
Weld Strength		ASTM D638	35.0	Mpa
Elongation at Break		ASTM D638	0.30	%
Bar Flow Length	320°C, 500.0 μm		7.10	CM
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	225	Mpa
Bending modulus		ASTM D790	15000	Mpa
elongation	Break	ASTM D638	3.5	%
tensile strength		ASTM D638	165	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature			306	°C
Glass transition temperature			125	°C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	285	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 40°C, 95%RH		0.80	%
Shrinkage rate	Across FlowFlow : 1.00 mm		0.40	%
Shrinkage rate	Shrinkage rate	Flow : 1.00 mm		0.030	%
melt mass-flow rate	320°C/2.16 kg	ASTM D1238	84	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	10.0 GHz	ASTM D150	0.010
Dielectric constant	10.0 GHz	ASTM D150	3.80
Dielectric strength		ASTM D149	30	KV/mm
Volume resistivity		ASTM D257	1.0E+16	ohms·cm
Compared to the anti leakage trace index		UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.