Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.20 g/cm³ |
density | | ASTM D792 | 1.19 g/cm³ |
Specific volume | | ASTM D792 | 0.830 cm³/g |
melt mass-flow rate | | ASTM D1238 | 11 g/10min |
Shrinkage rate | | 内部方法 | 0.50-0.70 % |
Water absorption rate | | ASTM D570 | 0.15 % |
Water absorption rate | | ASTM D570 | 0.35 % |
Water absorption rate | | ASTM D570 | 0.58 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 70 |
Rockwell hardness | | ASTM D785 | 118 |
optical performance | Test Condition | Test Method | Test Result |
---|
refractive index | | ASTM D542 | 1.586 |
transmissivity | | ASTM D1003 | 88.0 % |
Haze ratio | | ASTM D1003 | 1.0 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-2 |
UL flame retardant rating | | UL 94 | V-0 |
Limiting Oxygen Index | | ASTM D2863 | 25 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 62.0 Mpa |
tensile strength | | ASTM D638 | 68.0 Mpa |
elongation | | ASTM D638 | 7.0 % |
elongation | | ASTM D638 | 130 % |
Flexural modulus | | ASTM D790 | 2340 Mpa |
bending strength | | ASTM D790 | 96.0 Mpa |
Taber abraser | | ASTM D1044 | 10.0 mg |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 800 J/m |
Suspended wall beam without notch impact strength | | ASTM D4812 | 3200 J/m |
Dart impact | | ASTM D3029 | 169 J |
Impact strength of cantilever beam gap | | ASTM D1822 | 577 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Hot wire ignition (HWI) | | UL 746 | PLC 2 |
dielectric strength | | ASTM D149 | 15 KV/mm |
dielectric constant | | ASTM D150 | 3.17 |
dielectric constant | | ASTM D150 | 3.17 |
dielectric constant | | ASTM D150 | 2.96 |
Dissipation Factor | | ASTM D150 | 9E-04 |
Dissipation Factor | | ASTM D150 | 9E-04 |
Dissipation Factor | | ASTM D150 | 0.010 |
Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
High arc combustion index (HAI) | | UL 746 | PLC 1 |
High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 2 |
Volume resistivity | | ASTM D257 | >1.0E+17 ohms·cm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 137 °C |
Heat distortion temperature | | ASTM D648 | 132 °C |
vicat | | ASTM D15256 | 154 °C |
Linear coefficient of thermal expansion | | ASTME831 | 6.8E-05 cm/cm/°C |
specific heat | | ASTMC351 | 1250 J/kg/°C |
thermal conductivity | | ASTMC177 | 0.27 W/m/K |
RTI Elec | | UL 746 | 130 °C |
RTI Imp | | UL 746 | 130 °C |
RTI | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.