PA6 ZISAMIDE® M-BF160-N5
7
CompareTechnical Data Sheet
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| process temperature | 230-250 °C | ||
| Temperature | 80 °C | ||
| Melt Temperature | 220 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy impact strength | ASTM D256/ISO 179 | 4.5 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | ASTM D790/ISO 178 | 2800 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 115 kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 75 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | |
| Mold Shrinkage | ASTM D955 | 1.31 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 235 °C; 5 kg cm3/(10min) : 110 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL94 | v2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.