Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.55 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 14.0 cm³/10min |
| Shrinkage rate | | ISO 2577 | 0.90 % |
| Shrinkage rate | | ISO 2577 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| Viscosity value | | ISO 1628 | 106.4 ml/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 220 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | 内部方法 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 10500 MPa |
| tensile strength | Break | ISO 527-2/5 | 155 MPa |
| Tensile strain | Break | ISO 527-2/5 | 2.5 % |
| Flexural modulus | | ISO 178 | 9000 MPa |
| bending strength | | ISO 178 | 220 MPa |
| bending strength | | ISO 178 | 210 MPa |
| Bending Strain | | ISO 178 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 28 kV/mm |
| relative permittivity | | IEC 60250 | 4.00 |
| relative permittivity | | IEC 60250 | 3.80 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | 205 °C |
| Heat distortion temperature | | ISO 75-2/C | 125 °C |
| vicat | | ISO 306/B50 | 225 °C |
| melting temperature | | ISO 11357-3 | 220to255 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.