ABS

ABS Duroloy® AS-81 UNIGEL BRAZIL

Usages:
Applications in the automotive electrical and electronic fields
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	340 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	600 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield	ASTMD638	5.0 %
elongation	elongation	Break	ASTMD638	130 %
Bending modulus		ASTMD790	2300 MPa
Tensile modulus		ASTMD638	2200 MPa
tensile strength	Yield	ASTMD638	53.0 MPa
tensile strength	tensile strength	Break	ASTMD638	53.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	127 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	109 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	109 °C
Vicat softening temperature	--	ASTMD15252	135 °C
Vicat softening temperature	Vicat softening temperature	--	ASTMD15253	133 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTMD792	1.15 g/cm³
melt mass-flow rate	260°C/5.0kg	ASTMD1238	12 g/10min
Shrinkage rate	MD	ASTM D955	0.55to0.75 %
Water absorption rate	23°C,24hr	ASTM D570	0.20 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.