Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.940 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 0.70 g/10min |
| Vinyl acetate content | | | 18.0 wt% |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 89 |
| Shore hardness | | ASTM D2240 | 39 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 92 |
| Haze ratio | | ASTM D1003 | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 33.0 MPa |
| elongation | | ASTM D638 | 680 % |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D882 | 38.0 MPa |
| Elmendorf tear strength | | ASTM D1922 | 210 g |
| Elmendorf tear strength | | ASTM D1922 | 320 g |
| Tensile strain | | ASTM D882 | 700 % |
| Dart impact | | ASTM D1709B | 950 g |
| tensile strength | | ASTM D882 | 33.0 MPa |
| Tensile strain | | ASTM D882 | 820 % |
| Secant modulus | | ASTM D882 | 39.0 MPa |
| Secant modulus | | ASTM D882 | 38.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D15252 | 70.0 °C |
| melting temperature | | ASTM D3418 | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.