Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | JIS K-7112 | 1.04-1.06 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 3-6 10 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | JIS K-7210 | 2.3 g/10min |
| Water absorption rate | | JIS K-7209 | 0.07-0.08 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | JIS K-7110 | 10 kg-cm/cm of notch |
| elongation at break | | JIS K-7113 | 50 % |
| bending strength | | JIS K-7203 | 460 kg/cm |
| Rubbing modulus | | JIS K-7203 | 2.1 10 |
| tensile strength | | JIS K-7113 | 330 kg/cm |
| Rockwell hardness | | JIS K-7202 | R105 R,MScale |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D-257 | >10 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | JIS K-7206 | 95 °C |
| Linear coefficient of thermal expansion | | ASTM D-696 | 7-8 10 |
| flammability | | UL 94 | HB |
| Heat distortion temperature | | JIS K-7207 | 84 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.