Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.80 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 4.2 % |
| Water absorption rate | | ISO 62 | 1.2 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | HB |
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 24 % |
| FMVSS flammability | | FMVSS 302 | SE |
| | ISO 6452 | 4.0E-4 g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 17000 Mpa |
| Tensile stress | | ISO 527-2 | 250 Mpa |
| Tensile strain | | ISO 527-2 | 2.3 % |
| Tensile creep modulus | | ISO 899-1 | -- Mpa |
| Tensile creep modulus | | ISO 899-1 | -- Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 90 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 1.40 g/cm³ |
| Ejection Temperature | | | 210 °C |
| Specific Heat Capacity of Melt | | | 1870 J/kg/°C |
| Thermal Conductivity of Melt | | | 0.31 W/m/K |
| Emission of Organic Compounds | | VDA 277 | 6.50 µgC/g |
| Odor | | VDA 270 | 3.00 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 62631-3-2 | -- ohms |
| Volume resistivity | | IEC 62631-3-1 | 1.0E+13 ohms·m |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 285 到 305 °C |
| Melt Temperature, Optimum | | | 295 °C |
| Temperature | | | 50 到 90 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 到 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 262 °C |
| Heat distortion temperature | | ISO 75-2/A | 260 °C |
| Glass transition temperature 3 | | ISO 11357-2 | 80.0 °C |
| vicat | | ISO 306/B50 | 255 °C |
| Melting temperature 3 | | ISO 11357-3 | 262 °C |
| | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| thermal conductivity | | | 0.46 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices