Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | | 1.07to1.08 |
| saturation | | % | 1.8to4.0 |
| flow | | mm/mm | 71.1E-3-0.635 |
| balance | | % | 0.37to1.7 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | | 35.03to129.66 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 0.882to3.992 |
| Impact strength of simply supported beam without notch | | kJ/m² | 17.642to22.286 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | % | 4.5to6.9 |
| fracture | | % | 2.4to300 |
| fracture | | % | 3.0to54 |
| fracture | | | 30.9to110.34 Mpa |
| bending strength | | | 22.0to95.86 Mpa |
| yield | | | 34.83to65.24 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Surface Resistivity | | ohms | 1.0E+10到2.5E+14 |
| Volume resistivity | | ohms·cm | 1.0E+11到1.5E+12 |
| dielectric strength | | V/mil | 760to1100 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 112to160 |
| melting temperature | | °C | 215to225 |
| horizontal | | mm/mm/°C | 111.8E-5-203.2E-5 |
| flow | | mm/mm/°C | 27.9E-5-25.4E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.