| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.20 g/cm³ |
| melt mass-flow rate | | ISO1133 | 22 g/10min |
| Shrinkage rate | | ISO294-4 | 0.50到0.70 % |
| Shrinkage rate | | ISO294-4 | 0.50到0.70 % |
| Water absorption rate | | ISO62 | 0.14 % |
| Water absorption rate | | ISO62 | 0.30 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.585 |
| transmissivity | | ASTMD1003 | 89.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Hot filament ignition temperature | | IEC60695-2-13 | 850 °C |
| Limiting Oxygen Index | | ASTMD2863 | 26 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2300 MPa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 80 % |
| Flexural modulus | | ISO178 | 2500 MPa |
| Bending stress | | ISO178 | 80.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 20 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | | ASTMD256 | 500 J/m |
| Impact strength of cantilever beam gap | | ISO180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 20 kV/mm |
| CTI | | IEC60112 | 225 V |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/A50 | 148 °C |
| BallPressure Test | | IEC60695-10-2 | 通过 |
| | ASTMD696 | 7E-05 cm/cm/°C |
| | ISO75-2/A | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.