Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.6-1.5 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 1.56 g/cm³ |
| Water absorption rate | | ASTM D-570 | 0.10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D-638 | 3 % |
| bending strength | | ASTM D-790 | 160 Mpa |
| Izod notched impact strength | | ASTM D-256 | 60 J/m |
| Izod notched impact strength | | ASTM D-256 | 350 J/m |
| Flexural modulus | | ASTM D-790 | 6000 Mpa |
| tensile strength | | ASTM D-638 | 100 Mpa |
| tensile strength | | ASTM D638/ISO 527 | 100 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 6000 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 160 kg/cm²(MPa)[Lb/in²] |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | 3 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D-149 | 21 KV/mm |
| dielectric constant | | ASTM D-150 | 3.4 |
| | ASTM D-257 | 1016 Ω.cm |
| Dielectric loss | | ASTM D-150 | 0.02 |
| dielectric constant | | ASTM D150/IEC 60250 | 3.4 |
| Volume resistivity | | ASTM D257/IEC 60093 | 1016 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.56 |
| Mold Shrinkage | | ASTM D955 | 0.6-1.5 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| combustibility | | UL 94 | V-0 |
| Heat distortion temperature | | ASTM D-648 | 215 °C |
| Heat distortion temperature | | ASTM D-648 | 200 °C |
| Heat distortion temperature | | ASTM D648/ISO 75 | 215 ℃（℉） |
| Heat distortion temperature | | ASTM D648/ISO 75 | 200 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.