POM GH-25
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | GB/T3682-2000 | 1.52 g/10min |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO1133 | 2.7 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact Strength | ISO179-1 | 6.6 KJ/㎡ | |
| tensile strength | ISO527-1.2 | 133.4 MPa | |
| bending strength | ISO178 | 183.8 MPa | |
| Charpy Notched Impact Strength | GB/T1043.1-2008 | 8.78 KJ/m² | |
| yield stress | GB/T1040.1，2-2006 | 123.6 MPa | |
| Tensile modulus | GB/T1042.1，2-2006 | 9463 MPa | |
| Nominal fracture strain | GB/T1042.1，2-2006 | 10.32 % | |
| bending strength | ------- | 185.9 MPa | |
| Glass Fiber Content | ------- | 24.92 MPa | |
| hardness | 79.9 hrm | ||
| Flexural modulus | 7554 MPa |
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| Shrinkage rate | 0.87 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Load thermal deformation temperature | ISO75-1.2 | 158.2 ℃ | |
| DTUL | ------- | 157.9 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.