Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.045到0.20 % |
| Water absorption rate | | ISO62 | 0.18到0.21 % |
| Water absorption rate | | ISO62 | 0.23到0.91 % |
| density | | ASTMD792 | 1.44到1.71 g/cm³ |
| density | | ISO1183 | 1.38到1.78 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.17到0.53 % |
| Shrinkage rate | | ASTMD955 | 0.54到1.1 % |
| Shrinkage rate | | ISO294-4 | 0.20到1.0 % |
| Water absorption rate | | ASTMD570 | 0.044到0.061 % |
| Water absorption rate | | ISO62 | 0.040到0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 116到122 |
| Rockwell hardness | | ISO2039-2 | 99到123 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTMD2863 | 24到32 % |
| Limiting Oxygen Index | | ISO4589-2 | 19到36 % |
| Burning wire flammability index | | IEC60695-2-12 | 743到960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 650到968 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO527-2 | 125到161 MPa |
| tensile strength | | ASTMD638 | 96.3到197 MPa |
| tensile strength | | ISO527-2 | 78.4到210 MPa |
| tensile strength | | ASTMD638 | 0.866到195 MPa |
| compressive strength | | ASTMD695 | 136到235 MPa |
| elongation | | ASTMD638 | 2.0到4.0 % |
| elongation | | ISO527-2 | 2.0 % |
| elongation | | ASTMD638 | 2.0到3.4 % |
| elongation | | ISO527-2 | 1.4到3.2 % |
| Flexural modulus | | ASTMD790 | 5790到13800 MPa |
| Flexural modulus | | ISO178 | 3900到12300 MPa |
| bending strength | | ASTMD790 | 1.64到290 MPa |
| bending strength | | ISO178 | 129到271 MPa |
| bending strength | | ASTMD790 | 148到223 MPa |
| bending strength | | ASTMD790 | 170到222 MPa |
| Tensile modulus | | ASTMD638 | 4200到16700 MPa |
| Tensile modulus | | ISO527-2 | 4500到19200 MPa |
| tensile strength | | ASTMD638 | 80.0到176 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 5.9到11 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 29到65 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 59到120 J/m |
| Impact strength of cantilever beam gap | | ISO180 | 5.9到10 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 5.00到6.05 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTMD256 | 260到970 J/m |
| Suspended wall beam without notch impact strength | | ISO180 | 29到46 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1.0E+13到1.0E+14 ohms |
| dielectric strength | | ASTMD149 | 19到34 kV/mm |
| Surface Resistivity | | IEC60093 | 7.6E+13到1.1E+15 ohms |
| Volume resistivity | | ASTMD257,IEC60093 | 1.0E+13到2.5E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 21到34 kV/mm |
| dielectric constant | | ASTMD150 | 3.00到4.02 |
| dielectric constant | | IEC60250 | 3.66 |
| Dissipation Factor | | ASTMD150 | 4.9E-3到0.022 |
| Dissipation Factor | | IEC60250 | 1.0E-3到0.020 |
| arc resistance | | ASTMD495 | 96.0到128 sec |
| CTI | | IEC60112 | 195到251 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 209到233 °C |
| Heat distortion temperature | | ISO75-2/A | 199到241 °C |
| Continuous use temperature | | ASTMD794 | 110到150 °C |
| | ISO11359-2 | 4.0E-6到3.4E-5 cm/cm/°C |
| | ASTME831 | 3.1E-5到1.1E-4 cm/cm/°C |
| | ISO11359-2 | 3.5E-5到1.2E-4 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.27到1.7 W/m/K |
| RTI Elec | | UL746 | 139到155 °C |
| RTI Imp | | UL746 | 75.0到155 °C |
| RTI | | UL746 | 75.0到155 °C |
| vicat | | ASTMD1525 | 234到241 °C |
| vicat | | ISO306 | 215到241 °C |
| melting temperature | | ISO3146 | 245到256 °C |
| melting temperature | | ISO11357-3 | 250到256 °C |
| melting temperature | | ASTMD3418 | 245到255 °C |
| | ASTMD696 | 1.9E-5到4.5E-5 cm/cm/°C |
| | ASTME831 | 4.0E-6到5.8E-5 cm/cm/°C |
| Heat distortion temperature | | ISO75-2/B | 219到252 °C |
| Heat distortion temperature | | ASTMD648 | 229到251 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.