POM 100P NC010 DUPON SHANGHAI

Form：Granules | Grade：Injection grade

Properties:

High toughness

Typical Applications:

Automotive sectorEngine partsCam

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Engine parts \| Cam
Properties:	High toughness

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	400	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	12	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	14	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	14	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	50	mm/min
UL flame retardant rating	0.8mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Atomization	refraction，F值	ISO 6452	91	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2950	Mpa
tensile strength	Yield	ISO 527-2	71.0	Mpa
Tensile strain	Yield	ISO 527-2	25	%
Nominal tensile fracture strain		ISO 527-2	45	%
Tensile creep modulus	1hr	ISO 899-1	2700	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1500	Mpa
Bending modulus		ISO 178	2850	Mpa
bending strength	3.5%Strain	ISO 178	77.0	Mpa
Poisson's ratio		ISO 527	0.35
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	178	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.1E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1E-04	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1.1E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	1E-04	cm/cm/°C
				Linear coefficient of thermal expansion	TD：AnnealingTemperature	ISO 11359-2	160	°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：AnnealingTime-Optional	ISO 11359-2	30.0	min/mm
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	155	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0	°C
Vicat softening temperature	--	ISO 306/A50	175	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	160	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.42	g/cm³
melt mass-flow rate		ISO 1133	2.6	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	2.20	cm3/10min
Shrinkage rate	TD	ISO 294-4	1.9	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	2.2	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.4	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30	%
MediumDensity			1.19	g/cm³
SpecificHeatCapacity of Melt			3000	J/kg/°C
ThermalConductivityofMelt			0.22	W/m/K
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	2E+13	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
Dielectric strength		IEC 60243-1	41	KV/mm
Relative permittivity	100Hz	IEC 60250	3.90
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.90
Dissipation factor	100Hz	IEC 60250	3.5E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	5.5E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	88
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	119
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	4.70	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.