PP Copolymer 25C10400
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 0.905 g/cm³ | |
| melt mass-flow rate | ISO1133 | 12 g/10min | |
| Shrinkage rate | 1.3 % | ||
| 1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB | |
| Hot filament ignition temperature | IEC60695-2-13 | 650 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | ISO180/1A | 2.0 kJ/m² | |
| ISO180/1A | 6.0 kJ/m² | ||
| Charpy Notched Impact Strength | ISO179/1eA | 2.5 kJ/m² | |
| ISO179/1eA | 3.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/5 | 1300 MPa | |
| Tensile stress | ISO527-2/5 | 28.0 MPa | |
| Tensile strain | ISO527-2/5 | 6.5 % | |
| ISO527-2/5 | 50 % | ||
| Flexural modulus | ISO178 | 1250 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/B | 88.0 °C | ||
| ISO75-2/A | 51.0 °C | ||
| vicat | ISO306/A | 151 °C | |
| ISO306/B | 67.0 °C | ||
| melting temperature | ISO11357 | 165 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.