EPE 5101G
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 0.85 g/10min | |
| density | ASTM D792 | 0.922 g/cm³ |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 58 | |
| Haze ratio | ASTM D1003 | 15 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film thickness | 51 µm | ||
| Thin film puncture strength | 内部方法 | 4.29 J | |
| 内部方法 | 71.2 N | ||
| 内部方法 | 11.0 J/cm³ | ||
| Secant modulus | ASTM D882 | 219 MPa | |
| ASTM D882 | 248 MPa | ||
| tensile strength | ASTM D882 | 9.79 MPa | |
| ASTM D882 | 11.0 MPa | ||
| ASTM D882 | 40.8 MPa | ||
| ASTM D882 | 38.4 MPa | ||
| elongation | ASTM D882 | 590 % | |
| ASTM D882 | 620 % | ||
| Dart impact | ASTM D1709B | >850 g | |
| Elmendorf tear strength | ASTM D1922 | 720 g | |
| ASTM D1922 | 1000 g | ||
| Initial sealing temperature | 内部方法 | 106 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525 | 105 °C | |
| melting temperature | 内部方法 | 121 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.