Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:69 |
| Thermosetting components | | | 100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.70 % |
| density | | ASTMD792 | 1.14 g/cm³ |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HeatSag | | ASTM D3769 | 4.06 mm |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 160 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 1900 MPa |
| Flexural modulus | | ASTM D790 | 1030 MPa |
| Flexural modulus | | ASTM D790 | 689 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 105 kN/m |
| elongation | | ASTM D412 | 75 % |
| tensile strength | | ASTM D412 | 22.1 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.