PPO XYRON™ G701H-7433 BU ASAHI JAPAN
9
- Properties:High temperature resistanFlame retardantFiller: Glass fiber reinf10% filler by weight
- Usages:Automotive interior partsIndustrial machinery
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.35to0.50 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.060 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服,23°C | ISO527-2 | 72.0 | Mpa |
| elongation | 断裂,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ISO178 | 3760 | Mpa |
| bending strength | 23°C | ISO178 | 130 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179 | 10 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 130 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 128 | °C | |
| Linear coefficient of thermal expansion | MD：-30到65°C | ISO11359-2 | 6E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 2.00mm | IEC60243-1 | 41 | KV/mm |
| Dielectric constant | 100Hz | IEC60250 | 2.90 | |
| 1MHz | IEC60250 | 2.90 | ||
| Dissipation factor | 100Hz | IEC60250 | 4E-04 | |
| 1MHz | IEC60250 | 8E-04 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.