PP 366-3 LCY TAIWAN

Form：Granules | Grade：Injection grade

Properties:

High rigidityhigh strengthhigh strengthExcellent rigidityExcellent extensibilityEasy to formHomopolymerHigh tensile strengthExcellent rigidityExcellent extensibilityGood formability

Typical Applications:

PP boardcoversmall home appliancesCharger casingsheetPackaging tapeWoven bagSealsHome appliance productssheetPackaging tapeWoven bagcontainer bagSealsHome appliance products

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	PP board \| cover \| small home appliances \| Charger casing \| sheet \| Packaging tape \| Woven bag \| Seals \| Home appliance products \| sheet \| Packaging tape \| Woven bag \| container bag \| Seals \| Home appliance products
Properties:	High rigidity \| high strength \| high strength \| Excellent rigidity \| Excellent extensibility \| Easy to form \| Homopolymer \| High tensile strength \| Excellent rigidity \| Excellent extensibility \| Good formability

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230℃，2.16kg	ASTM D-1238	3	g/10min
density		ASTM D-792	0.902	g/cm³
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ASTM D-638	35	Mpa
elongation	Yield	ASTM D-638	11	%
Bending modulus		ASTM D-790	1608	Mpa
Rockwell hardness		ASTM D-785	97	R scale
Impact strength of cantilever beam gap	23℃	ASTM D-256	3.5	kg.cm/cm
Rockwell hardness	R scale	ASTM D785	97
tensile strength	Yield	ASTM D638	36	Mpa
elongation	Yield	ASTM D638	11	%
Bending modulus		ASTM D790	1640	Mpa
Impact strength of cantilever beam gap	切口23℃	ASTM D256	3.5	kg-cm/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D-648	98	°C
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648	98	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM D-955	1.4	%
density		ASTM D792	0.902	g/cm³
melt mass-flow rate	230℃/2.16 kg	ASTM D1238	3.0	g/10min
Shrinkage rate		ASTM D955	1.4	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.