Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.05 g/cm³ |
| Melt volume flow rate | | ISO1133 | 6.00 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.50到0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 100 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 46.0 Mpa |
| Tensile strain | | ISO527-2 | 3.1 % |
| Tensile strain | | ISO527-2 | >15 % |
| Flexural modulus | | ISO178 | 2350 Mpa |
| Bending stress | | ISO178 | 73.0 Mpa |
| Tensile modulus | | ISO527-2 | 2400 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 23 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+16 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 38 KV/mm |
| | IEC60250 | 3.00 |
| | IEC60250 | 2.90 |
| Dissipation Factor | | IEC60250 | 6.5E-03 |
| Dissipation Factor | | IEC60250 | 8.5E-03 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature 3 | | ISO75-2/A | 98.0 °C |
| vicat | | ISO306/B50 | 107 °C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
| Hot deformation temperature 3 | | ISO75-2/B | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.