Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.70to1.90 g/cm³ |
| Shrinkage rate | | ASTM D1895 | 2.0 |
| Shrinkage rate | | ISO 2577 | 0.10to0.30 % |
| Water absorption rate | | ASTM D570 | 0.10to0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Barcol Hardness | | ASTM D2583 | 30to50 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 13800 MPa |
| tensile strength | | ASTM D638 | 48.3 MPa |
| Flexural modulus | | ASTM D790 | 13800 MPa |
| bending strength | | ASTM D790 | 124 MPa |
| compressive strength | | ASTM D695 | 159 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 430 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 11 kV/mm |
| arc resistance | | ASTM D495 | >180 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | >260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.