Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO1133 | 2.4 g/10min |
| Melt volume flow rate | | ISO1133 | 1.90 cm³/10min |
| Shrinkage rate | | ISO294-4 | 2.0 % |
| Shrinkage rate | | ISO294-4 | 1.8 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 94 |
| Rockwell hardness | R-Scale | ISO2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FMVSS flammability | | FMVSS302 | B |
| burning rate | | ISO3795 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Flammability level | | IEC60695-11-10,-20 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <8.00 mg/kg |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 2900 MPa |
| Tensile modulus | | ISO527-2 | 3100 MPa |
| Tensile stress | Yield | ISO527-2 | 72.0 MPa |
| Tensile strain | Yield | ISO527-2 | 22 % |
| Nominal tensile fracture strain | | ISO527-2 | 40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 9.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 165 °C |
| Heat distortion temperature | | ISO75-2/A | 97.0 °C |
| melting temperature | | ISO11357-3 | 178 °C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.