Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Density/specific gravity 2 | | ASTMD792 | 1.20 g/cm³ |
| density | | ISO1183 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 22 g/10min |
| Melt volume flow rate | | ISO1133 | 22.0 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 77 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTMD790 | 2340 Mpa |
| Flexural modulus | | ISO178 | 2400 Mpa |
| bending strength | | ASTMD790 | 89.8 Mpa |
| Bending stress 5 | | ISO178 | 90.0 Mpa |
| tensile strength | | ASTMD638 | 61.6 Mpa |
| Tensile stress | | ISO527-2/50 | 63.0 Mpa |
| Tensile stress | | ISO527-2/50 | 70.0 Mpa |
| elongation | | ASTMD638 | 110 % |
| Tensile strain | | ISO527-2/50 | 120 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 60 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 780 J/m |
| Impact strength of cantilever beam gap | | ISO180/4A | 60 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature 6 | | ASTMD648 | 143 °C |
| Heat distortion temperature | | ISO75-2/A | 127 °C |
| Heat distortion temperature | | ISO75-2/A | 142 °C |
| vicat | | ISO306/A50 | 148 °C |
| vicat | | ISO306/B50 | 143 °C |
| | ISO11359-2 | 6.0E-5to8.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.