PA6 BKV30 000000 ENVALIOR WUXI

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedFiller: Glass fiber reinf30%Filler by weight

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Glass fiber reinforced | Filler: Glass fiber reinf | 30% | Filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	70	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	60	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	75	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	1.6mm	UL 94	HB
			UL flame retardant rating	3.0mm	UL 94	HB
			UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	600	°C
Extreme Oxygen Index		ISO 4589-2	22	%
BurningBehavior	>1.00mm	ISO 3795	passed
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ASTM D638	9200	Mpa
Tensile modulus	Tensile modulus	-5°C	ISO 527-2/1	9800	Mpa
elongation	Break,23°C	ASTM D638	3.0	%
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
Tensile creep modulus	1hr	ISO 899-1	--	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	--	Mpa
bending strength	3.5%Strain	ISO 178/A	--	Mpa
	bending strength	23°C	ISO 178	280	Mpa
		bending strength	FlexuralStrainatFlexuralStrength6(23°C)		4.0	%
		bending strength	bending strength	23°C	ASTM D790	280	Mpa
Bending modulus	23°C	ISO 178/A	8600	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	8270	Mpa
tensile strength	Break,23°C	ISO 527-2/5	180	Mpa
tensile strength	tensile strength	Break,23°C	ASTM D638	180	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	200	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	>200	°C
Melting temperature		ISO 11357-3	222	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	8E-05	cm/cm/°C
RTI Elec	1.5mm	UL 746	130	°C
RTI Imp	0.8mm	UL 746	95.0	°C
RTI Imp	RTI Imp	1.5mm	UL 746	95.0	°C
RTI Str	0.8mm	UL 746	130	°C
RTI Str	RTI Str	1.5mm	UL 746	130	°C
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ASTM D648	215	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200	°C
		Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ASTM D648	200	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density		ISO 60	0.70	g/cm³
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	14.0	cm3/10min
Shrinkage rate	TD:280°C,3.00mm2	ISO 2577	0.82	%
	Shrinkage rate	TD:120°C,2hr,3.00mm3	ISO 294-4	0.12	%
	Shrinkage rate	Shrinkage rate	MD:280°C,3.00mm2	ISO 2577	0.16	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.1	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	7.0	%
Shrinkage rate	MD:120°C,2hr,3.00mm3	ISO 2577	0.030	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	23°C,1MHz	IEC 60250	4.00
Dissipation factor	23°C,50Hz	IEC 60250	5E-03
	Dissipation factor	23°C,100Hz	IEC 60250	5E-03
	Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.0150.015
Arc resistance		ASTM D495	--	sec
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity	23°C	IEC 60093	1E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	40	KV/mm
Dielectric strength	Dielectric strength	23°C,3.00mm	IEC 60243-1	40	KV/mm
Dielectric constant	23°C,50Hz	IEC 60250	4.00
Dielectric constant	Dielectric constant	23°C,1MHz	IEC 60250	4.00
Relative permittivity	23°C,100Hz	IEC 60250	4.00
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	210	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
Thin film puncture strength	--7	ISO 6603-2	8.00	J
	Thin film puncture strength	--8	ISO 6603-2	6.00	J
		Thin film puncture strength	--8	ISO 6603-2	950	N
		Thin film puncture strength	Thin film puncture strength	--7	ISO 6603-2	1070	N
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6.GR.14-100.GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.