PA66 158L NC010 DUPONT USA

183

Form：Granules | Grade：Withdrawal level

Properties:

High rigidityhigh strengthHigh impact resistance

Typical Applications:

MechatronicsAutomotive components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Mechatronics \| Automotive components
Properties:	High rigidity \| high strength \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
FMVSS flammability		FMVSS302	B
Extreme Oxygen Index		ISO 4589-2	25	%
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	0.9mm	IEC 60695-11-10,-20	HB
Burning rate	1.00mm	ISO 3795	<100	mm/min
UL flame retardant rating	0.9mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	2050	Mpa
Nominal tensile fracture strain		ISO 527-2	35	%
Tensile strain	Yield	ISO 527-2	4.5	%
tensile strength	Yield	ISO 527-2	62.0	Mpa
Tensile modulus		ISO 527-2	2400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.8E-04	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1.2E-04	cm/cm/°C
			Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	1.7E-04	cm/cm/°C
				Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.2E-04	cm/cm/°C
Melting temperature		ISO 11357-3	218	°C
Glass transition temperature		ISO 11357-2	60.0	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	62.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	135	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
ThermalConductivityofMelt			0.19	W/m/K
SpecificHeatCapacity of Melt			2800	J/kg/°C
MediumDensity			0.900	g/cm³
Shrinkage rate	MD：3.20mm		1.1	%
	Shrinkage rate	TD	ISO 294-4	1.4	%
	Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.3	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	3.0	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.3	%
Stickiness		ISO 307	120	cm³/g
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	36	KV/mm
Relative permittivity	100Hz	IEC 60250	3.60
Surface resistivity		IEC 60093	--	ohms
Relative permittivity	1MHz	IEC 60250	3.20
Dissipation factor	100Hz	IEC 60250	0.014
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.016

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 158L NC010 DUPONT USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index