Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.21 g/cm³ |
| density | | ASTM D792 | 1.22 g/cm³ |
| Specific volume | | ASTM D792 | 0.835 cm³/g |
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| Shrinkage rate | | 内部方法 | 0.50-0.70 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| Water absorption rate | | ASTM D570 | 0.35 % |
| Water absorption rate | | ASTM D570 | 0.58 % |
| Outdoor applicability | | UL 746C | f1 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 118 |
| Rockwell hardness | | ASTM D785 | 70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 35 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 525 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 640 J/m |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 3200 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 62.1 Mpa |
| tensile strength | | ASTM D638 | 55.8 Mpa |
| elongation | | ASTM D638 | 7.0 % |
| elongation | | ASTM D638 | 90 % |
| Flexural modulus | | ASTM D790 | 2240 Mpa |
| bending strength | | ASTM D790 | 91.0 Mpa |
| Taber abraser | | ASTM D1044 | 10.0 mg |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 17 KV/mm |
| dielectric constant | | ASTM D150 | 3.01 |
| dielectric constant | | ASTM D150 | 3.01 |
| dielectric constant | | ASTM D150 | 2.96 |
| Dissipation Factor | | ASTM D150 | 9E-04 |
| Dissipation Factor | | ASTM D150 | 9E-04 |
| Dissipation Factor | | ASTM D150 | 0.010 |
| arc resistance | | ASTM D495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 |
| High arc combustion index (HAI) | | UL 746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 138 °C |
| Heat distortion temperature | | ASTM D648 | 132 °C |
| vicat | | ASTM D15256 | 152 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 6.8E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.19 W/m/K |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 120 °C |
| RTI | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.